ESAB Dual Shield II 100 Wire - .045" - 33 lb PSP VP - 245013636
Dual Shield II 100 is an all-position flux cored electrode that combines a high strength deposit with excellent impact toughness and low diffusible hydrogen levels. The rutile basic slag system produces a smooth spray-like transfer with reduced spatter and low post weld cleanup. Dual Shield II 100 is designed to join high strength steels such as HY-80 and T-1 in the as welded or stress relieved condition using a 75% Ar / 25% CO2 shielding gas. It is especially well suited for high tensile steels that are used in sub-zero temperatures. The weld metal analysis is similar to an E10018-M low hydrogen electrode.
Shielding Gas 75% Argon/25% CO2
-
Classifications/Approvals - ASME SFA 5.29
- AWS A5.29; E101T1-K3MH4
Depositions/Parameters:
| .035 in, 0.9 mm | 130 A A | 22 | 288 ipm, 732 cm/min | 3.2 lbs./hr., 1.45 kg./hr. | 85 % | | 150 A A | 25 | 384 ipm, 975 cm/min | 4.3 lbs./hr., 1.95 kg./hr. | 85 % | | 200 A A | 27 | 576 ipm, 1463 cm/min | 6.5 lbs./hr., 2.95 kg./hr. | 85 % | | 250 A A | 30 | 784 ipm, 1991 cm/min | 8.9 lbs./hr., 4.04 kg./hr. | 86 % | | .045 in, 1.2 mm | 150 A A | 28 | 200 ipm, 508 cm/min | 4.2 lbs./hr., 1.91 kg./hr. | 86 % | | 210 A A | 29 | 300 ipm, 762 cm/min | 6.3 lbs./hr., 2.86 kg./hr. | 86 % | | 250 A A | 30 | 400 ipm, 1016 cm/min | 8.5 lbs./hr., 3.86 kg./hr. | 87 % | | 290 A A | 33 | 500 ipm, 1270 cm/min | 10.7 lbs./hr., 4.85 kg./hr. | 87 % | | 330 A A | 34 | 600 ipm, 1524 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 87 % | | .052 in, 1.4 mm | 155 A A | 25 | 150 ipm, 381 cm/min | 4.4 lbs./hr., 2 kg./hr. | 87 % | | 245 A A | 28 | 250 ipm, 635 cm/min | 7.3 lbs./hr., 3.31 kg./hr. | 86 % | | 310 A A | 33 | 350 ipm, 889 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 85 % | | 360 A A | 36 | 450 ipm, 1143 cm/min | 13.3 lbs./hr., 6.03 kg./hr. | 85 % | | 430 A A | 37 | 600 ipm, 1524 cm/min | 17.6 lbs./hr., 7.98 kg./hr. | 87 % | | 1/16 in, 1.6 mm | 190 A A | 27 | 150 ipm, 38 cm/min | 6.1 lbs./hr., 2.77 kg./hr. | 87 % | | 300 A A | 30 | 250 ipm, 635 cm/min | 10.2 lbs./hr., 4.63 kg./hr. | 87 % | | 365 A A | 33 | 300 ipm, 762 cm/min | 12.3 lbs./hr., 5.58 kg./hr. | 86 % | | 410 A A | 33 | 350 ipm, 889 cm/min | 14 lbs./hr., 6.35 kg./hr. | 88 % | | 450 A A | 33 | 400 ipm, 1016 cm/min | 16.1 lbs./hr., 7.3 kg./hr. | 87 % | | 500 A A | 39 | 500 ipm, 1270 cm/min | 20.1 lbs./hr., 9.11 kg./hr. | 87 % | | 5/64 in, 2.0 mm | 250 A A | 26 | 112 ipm, 284 cm/min | 6.4 lbs./hr., 2.9 kg./hr. | 85 % | | 350 A A | 28 | 176 ipm, 447 cm/min | 10.5 lbs./hr., 4.76 kg./hr. | 85 % | | 450 A A | 31 | 258 ipm, 655 cm/min | 14.8 lbs./hr., 6.71 kg./hr. | 85 % | | 3/32 in, 2.4 mm | 350 A A | 30 | 124 ipm, 315 cm/min | 9.6 lbs./hr., 4.35 kg./hr. | 84 % | | 400 A A | 30 | 166 ipm, 422 cm/min | 12.7 lbs./hr., 5.76 kg./hr. | 85 % | | 450 A A | 31 | 197 ipm, 500 cm/min | 15 lbs./hr., 6.8 kg./hr. | 86 % | | 500 A A | 32 | 237 ipm, 602 cm/min | 18.5 lbs./hr., 8.39 kg./hr. | 86 % | | 550 A A | 34 | 278 ipm, 706 cm/min | 21.3 lbs./hr., 9.66 kg./hr. | 88 % | | 7/64 in, 2.8 mm | 550 A A | 30 | 140 ipm, 356 cm/min | 17.1 lbs./hr., 7.76 kg./hr. | 85 % | | 625 A A | 34 | 161 ipm, 409 cm/min | 19.6 lbs./hr., 8.89 kg./hr. | 86 % | | 700 A A | 36 | 190 ipm, 483 cm/min | 23 lbs./hr., 10.43 kg./hr. | 86 % | | 1/8 in, 3.2 mm | 600 A A | 32 | 111 ipm, 282 cm/min | 16.2 lbs./hr., 7.35 kg./hr. | 86 % | | 725 A A | 34 | 153 ipm, 389 cm/min | 22.5 lbs./hr., 10.21 kg./hr. | 86 % | | 850 A A | 38 | 194 ipm, 93 cm/min | 29.2 lbs./hr., 13.25 kg./hr. | 85 % |
Properties:
| As Welded 75% Ar / 25% CO2 | | | Yield Strength | 101 ksi, 700 MPa | | Tensile Strength | 109 ksi, 755 MPa | | Reduction in Area | 60 % | | Elongation in 2" | 21 % | | Stress Relieved 1 hr. @ 1050ºF (566ºC) 75% Ar / 25% CO2 | | | Yield Strength | 99 ksi, 685 MPa | | Tensile Strength | 110 ksi, 760 MPa | | Reduction in Area | 61 % | | Elongation in 2" | 22 % | | Typical Charpy V-Notch Impact Properties | | | Testing Temperature 0ºF (-18ºC) | | | As Welded 75% Ar / 25% CO2 | 48 ft.-lbs., 65 J | | Stress Relieved 1 hr. @ 1050ºF (566ºC) 75% Ar / 25% CO2 | 33 ft.-lbs., 45 J | | Testing Temperature -20ºF (-29ºC) | | | As Welded 75% Ar / 25% CO2 | 40 ft.-lbs., 54 J | | Stress Relieved 1 hr. @ 1050ºF (566ºC) 75% Ar / 25% CO2 | 30 ft.-lbs., 41 J | | Testing Temperature -40ºF (-40ºC) | | | As Welded 75% Ar / 25% CO2 | 32 ft.-lbs., 43 J | | Testing Temperature -60ºF (-51ºC) | | | As Welded 75% Ar / 25% CO2 | 28 ft.-lbs., 38 J | | Typical Undiluted Weld Metal Analysis | | | 75% Ar / 25% CO2 | | | C | 0.05 % | | Mn | 1.45 % | | Si | .44 % | | P | .012 % | | S | .010 % | | Ni | 1.70 % | | Mo | 0.40 % |