ESAB Dual Shield 8000-Ni2 Wire - 1/16" - 33 lb AWS - 245020219

ESAB Dual Shield 8000-Ni2 Wire - 1/16" - 33 lb AWS - 245020219

Manufacturer: ESAB®
SKU: ESA245020219
Price: $191.23
Order Now

Quantity:


ESAB Dual Shield 8000-Ni2 Wire - 1/16" - 33 lb AWS - 245020219

Dual Shield 8000-Ni2 is an all-position flux cored electrode that deposits 2.5% Ni deposit with an 82 ksi (565 MPa) minimum tensile strength. Dual Shield 8000-Ni2 may be used with CO2 or Argon mixtures. The Argon-CO2 mixtures reduce spatter and further improve weldability especially for small vertical-up fillets. Dual Shield 8000-Ni2 produces superior weld metal properties which make it most desirable for such applications as shipbuilding and heavy machinery construction. The weld metal analysis is similar to an E8018-C1 low Hydrogen electrode.

Shielding Gas

100% CO2 or Argon - CO2 mixtures up to 80% Argon


  • Classifications/Approvals

    • ASME SFA 5.29
    • A.B.S.- 3YSA
    • AWS A5.29; E81T1-Ni2C/Ni2M
    • MIL-E-24403/1; MIL-81T1-Ni2C/Ni2M
    • CERTIFIED BY C.W.B.- AWS A5.29

Depositions/Parameters:

Diameter Amps Volts Wire Feed Speed Deposition Rate Efficiency
.035 in, 0.9 mm 130 A 22 288 ipm, 732 cm/min 3.2 lbs./hr., 1.45 kg./hr. 85 %
150 A 25 384 ipm, 975 cm/min 4.3 lbs./hr., 1.95 kg./hr. 85 %
200 A 27 576 ipm, 1463 cm/min 6.5 lbs./hr., 2.95 kg./hr. 85 %
250 A 30 784 ipm, 1991 cm/min 8.9 lbs./hr., 4.04 kg./hr. 86 %
.045 in, 1.2 mm 150 A 28 200 ipm, 508 cm/min 4.2 lbs./hr., 1.91 kg./hr. 86 %
210 A 29 300 ipm, 762 cm/min 6.3 lbs./hr., 2.86 kg./hr. 86 %
250 A 30 400 ipm, 1016 cm/min 8.5 lbs./hr., 3.86 kg./hr. 87 %
290 A 33 500 ipm, 1270 cm/min 10.7 lbs./hr., 4.85 kg./hr. 87 %
330 A 34 600 ipm, 1524 cm/min 12.7 lbs./hr., 5.76 kg./hr. 87 %
.052 in, 1.4 mm 155 A 25 150 ipm, 381 cm/min 4.4 lbs./hr., 2.00 kg./hr. 87 %
245 A 28 250 ipm, 635 cm/min 7.3 lbs./hr., 3.31 kg./hr. 86 %
310 A 33 350 ipm, 889 cm/min 10.2 lbs./hr., 4.63 kg./hr. 85 %
360 A 36 450 ipm, 1143 cm/min 13.3 lbs./hr., 6.03 kg./hr. 85 %
430 A 37 600 ipm, 1524 cm/min 17.6 lbs./hr., 7.98 kg./hr. 87 %
1/16 in, 1.6 mm 190 A 27 150 ipm, 381 cm/min 6.1 lbs./hr., 2.77 kg./hr. 87 %
300 A 30 250 ipm, 635 cm/min 10.2 lbs./hr., 4.63 kg./hr. 87 %
365 A 33 300 ipm, 762 cm/min 12.3 lbs./hr., 5.58 kg./hr. 86 %
410 A 33 350 ipm, 889 cm/min 14 lbs./hr., 6.35 kg./hr. 88 %
450 A 33 400 ipm, 1016 cm/min 16.1 lbs./hr., 7.30 kg./hr. 87 %
500 A 39 500 ipm, 1270 cm/min 20.1 lbs./hr., 9.11 kg./hr. 87 %
5/64 in, 2.0 mm 250 A 26 112 ipm, 284 cm/min 6.4 lbs./hr., 2.90 kg./hr. 85 %
350 A 28 176 ipm, 447 cm/min 10.5 lbs./hr., 4.76 kg./hr. 85 %
450 A 31 258 ipm, 655 cm/min 14.8 lbs./hr., 6.71 kg./hr. 85 %
3/32 in, 2.4 mm 350 A 30 124 ipm, 315 cm/min 9.6 lbs./hr., 4.35 kg./hr. 84 %
400 A 30 166 ipm, 422 cm/min 12.7 lbs./hr., 5.76 kg./hr. 85 %
450 A 31 197 ipm, 500 cm/min 15 lbs./hr., 6.80 kg./hr. 86 %
500 A 32 237 ipm, 602 cm/min 18.5 lbs./hr., 8.39 kg./hr. 86 %
550 A 34 278 ipm, 706 cm/min 21.3 lbs./hr., 9.66 kg./hr. 88 %
7/64 in, 2.8 mm 550 A 30 140 ipm, 356 cm/min 17.1 lbs./hr., 7.76 kg./hr. 85 %
625 A 34 161 ipm, 409 cm/min 19.6 lbs./hr., 8.89 kg./hr. 86 %
700 A 36 190 ipm, 483 cm/min 23 lbs./hr., 10.43 kg./hr. 86 %
1/8 in, 3.2 mm 600 A 32 111 ipm, 282 cm/min 16.2 lbs./hr., 7.35 kg./hr. 86 %
725 A 34 153 ipm, 389 cm/min 22.5 lbs./hr., 10.21 kg./hr. 86 %
850 A 38 194 ipm, 493 cm/min 29.2 lbs./hr., 13.25 kg./hr. 85 %



Procedures:

As Welded 75% Ar / 25% CO2  
Yield Strength 82 ksi, 565 MPa
Tensile Strength 90 ksi, 620 MPa
Reduction in Area 68 %
Elongation in 2" 27 %
As Welded CO2  
Yield Strength 80 ksi, 550 MPa
Tensile Strength 88 ksi, 605 MPa
Reduction in Area 67 %
Elongation in 2" 26 %
Typical Charpy V-Notch Impact Properties  
Testing Temperature 0ºF (-18ºC)  
As Welded CO2 62 ft.-lbs., 84 J
As Welded 75% Ar / 25% CO2 63 ft.-lbs., 69 J
Testing Temperature -20ºF (-29ºC)  
As Welded CO2 43 ft.-lbs., 58 J
As Welded 75% Ar / 25% CO2 47 ft.-lbs., 64 J
Testing Temperature -40ºF (-40ºC)  
As Welded CO2 39 ft.-lbs., 53 J
As Welded 75% Ar / 25% CO2 40 ft.-lbs., 54 J
Typical Undiluted Weld Metal Analysis  
CO2  
C .05 %
Mn 0.9 %
Si 0.3 %
P .012 %
S .010 %
Ni 2.2 %
75% Ar / 25% CO2  
C .05 %
Mn 1.1 %
Si 0.4 %
P .012 %
S .010 %
Ni 2.2 %